Preparation and characterization of Fe2O3-TiO2-MnO2/Al2O3 catalysts
ZHANG Yao-hui1, TU Yong1, TANG Min1, XU Jun1, LIU Wei-jin2, WU Qian1, CHEN Yong1, LI Jun1
1. Jiangsu Provincial Academy of Environmental Science, Jiangsu Key Laboratory of Environmental Engineering, Nanjing 210036, China; 2. Jiangsu Environmental Engineering Consulting Center, Nanjing 210036, China
Abstract:The Fe2O3-TiO2-MnO2/Al2O3 oxide catalyst was prepared by the dipping-calcination method using A12O3 as a carrier. SEM, EDX, BET and XRD techniques were performed to characterize the catalyst. The catalytic activity of the prepared catalyst was investigated by catalytic ozonation of the effluent in sewage plant of chemical industry park at room temperature and atmospheric pressure. The results showed that the optimal preparation parameters were as follow: the molar ratio of Ti4+, Mn2+ and Fe3+ in the dipping solution was 2:2:1, calcination time and temperature 4h and 500℃ respectively. Furthermore, the degradation performance obtained for COD in wastewater showed that the catalytic activity of Fe2O3-TiO2-MnO2/Al2O3 catalyst was good when amount of ozone was 50mg·L-1 and filling ratio of catalyst was 50%, it could be removed 52.2% of COD after 60min oxidation. Three-dimensional fluorescence spectra showed that visible humus and UV humus in the wastewater were completely degraded after catalytic ozonation, and a small amount of fulvic was generated.
Wang J B, Zhou Y R, Zhu W P, et al. Catalytic ozonation of dimethyl phthalate and chlorination disinfection by-product precursors over Ru/AC [J]. Journal of Hazardous Materials, 2009,166:502-507.
[3]
Michael C, Violet A O, Wim T M, et al. Ozonation of biologically treated landfill leachate: efficiency and insights in organic conversions [J]. Chemical Engineering Journal, 2015,277:104-111.
[4]
Frauke L, Stefanie H, Claudia G, et al. Removal of total and antibiotic resistant bacteria in advanced wastewater treatment by ozonation in combination with different filtering techniques [J]. Water Research, 2015,69:243-251.
Kim H C, Choi W J, Maeng S K, et al. Ozonation of piggery wastewater for enhanced removal of contaminants by S. quadricauda and the impact on organic characteristics [J]. Bioresource Technology, 2014,159:128-135.
[7]
Andy H, Ting X. Treatment of oil spill water by ozonation and sand filtration [J]. Chemosphere, 2013,91:641-647.
[8]
Merlea T, Pic J S, Manerob M H, et al. Influence of activated carbons on the kinetics and mechanisms of aromatic molecules ozonation [J]. Catalysis Today, 2010,151:166-172.
[9]
Tong S P, Liu W P, Leng W H, et al. Characteristics of MnO2 catalytic ozonation of sulfosalicylic acid and propionic acid in water [J]. Chemosphere, 2003,53:1359-1364.
[10]
Wu J J, Murgandham M, Chang L T, et al. Catalytic ozonation of oxalic acid using SrTiO3 catalyst [J]. Ozone Science & Engineering, 2011,33:74-79.
[11]
Quispe C, Villasenor J, Pecchi G, et al. Catalytic ozonation of oxalic acid with MnO2/TiO2 and Rh/TiO2 [J]. J. Chil. Chem. Soc., 2006,51:1049-1052.
[12]
Hakim D, Olivier C, Benoit C, et al. Influences of pH, temperature and activated carbon properties on the interaction ozone/activated carbon for a wastewater treatment process [J]. Desalination, 2010,254:12-16.
[13]
Gracia R, Cortes S, Sarasa J. TiO2-catalysed ozonation of raw Ebro river water [J]. Water Research, 2000,34:1525-1532.
[14]
Lv A H, Hu C, Nie Y L, et al. Catalytic ozonation of toxic pollutants over magnetic cobalt and manganese co-doped γ-Fe2O3[J]. Applied Catalysis B: Environmental, 2010,100:62- 67.
[15]
Dong Y M, Yang H X, He K, et al. β-MnO2nanowires: A novel ozonation catalyst for water treatment [J]. Applied Catalysis B: Environmental, 2009,85:155-161.
[16]
Wang J B, Cheng J Y, Wang C, et al. Catalytic ozonation of dimethyl phthalate with RuO2/Al2O3 catalysts prepared by microwave irradiation [J]. Catalysis Communications, 2013,43: 1-5.
[17]
Alvarez P M, Beltran F J, Pocostales J P, et al. Preparation and structural characterization of Co/Al2O3 catalysts for the ozonation of pyruvic acid [J]. Applied Catalysis B: Environmental, 2007,72:322-330.
[18]
Rezaeia F, Moussavib G, Bakhtiaria A R, et al. Toluene removal from waste air stream by the catalytic ozonationprocess with MgO/GAC composite as catalyst [J]. Journal of Hazardous Materials, 2016,306:348-358.
Pons M N, Bont S L, Potier O,et al. Spectral analysis and fingerprinting for biomedia characterization [J]. Journal of Biotechnology, 2004,113(6):211-230.