Fe/TiO2-x可见光活化过硫酸盐降解双酚A的作用机制

Abstract
Figure/Table
References
Related Citation (6)

Download: PDF (4536 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract In this study, TiO₂ and FeCl₃ was used as raw materials, Fe/TiO₂_-X catalysts with high visible light catalytic activity were successfully prepared by hydrothermal-calcination method and applied to the catalytic degradation of BPA by persulfate. The results showed that this system has excellent catalytic oxidation ability, the degradation rate of BPA (50mg/L) reached 100% in 40min, and the salinity reached 68.92%. At the same time, the effects of self-doped Ti³⁺ in the composite and the amount of catalyst and PS concentration on the degradation of organic compounds were studied. This system can realize the efficient cycle of trivalent iron and divalent iron by autogenic photoelectron reduction of Fe³⁺. Sulfate radical (SO₄^-•) and hydroxyl radical (•OH) were the main active oxidizing substances in the system, of which the contribution rate of •OH is more than 66.2%. The result also showed that alkaline environment and inorganic anions such as CO₃^2- had negative effect on the performance of the system.

Key words： degradation of organic micro-pollutants advanced persulfate oxidation visible-light photocatalysis Ti³⁺ self-doped TiO₂ Fe quantum dots

Received: 06 November 2022

PACS:

X703.1

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	FU Quan-chao
	XU Lu
	LIU Pei-hua
	JIN Xin
	JIN Peng-kang

Cite this article:

FU Quan-chao,XU Lu,LIU Pei-hua等. Characteristics and mechanism of bisphenol A degradation by persulfate activated by Fe/TiO₂_-_X under visible light[J]. CHINA ENVIRONMENTAL SCIENCECE, 2023, 43(6): 2841-2852.

URL:

http://www.zghjkx.com.cn/EN/ OR http://www.zghjkx.com.cn/EN/Y2023/V43/I6/2841

[1] Wang J, Wang S. Activation of persulfate (PS) and peroxymonosulfate (PMS) and application for the degradation of emerging contaminants[J]. Chemical Engineering Journal, 2018,334:1502-1517.
[2] Ghanbari F, Moradi M. Application of peroxymonosulfate and its activation methods for degradation of environmental organic pollutants:Review[J]. Chemical Engineering Journal, 2017,310:41-62.
[3] Chen X, Liu L, Yu P Y, et al. Increasing solar absorption for photocatalysis with black hydrogenated titanium dioxide nanocrystals[J]. Science, 2011,331(6018):746-750.
[4] Chen X, Liu L, Huang F. Black titanium dioxide (TiO₂) nanomaterials[J]. Chemical Society Reviews, 2015,44(7):1861-1885.
[5] Nahid Pervez M, Ying Wei, Peipei Sun,et al. α-FeOOH quantum dots impregnated graphene oxide hybrids enhanced arsenic adsorption:The mediation role of environmental organic ligands[J].Science of The Total Environment, 2021,0048:96-97.
[6] Duan X, Sun H, Wang Y, et al. N-doping-induced nonradical reaction on single-walled carbon nanotubes for catalytic phenol oxidation[J]. ACS Catalysis, 2014,5(2):553-559.
[7] Wang Y, Zhao X, Cao D, et al. Peroxymonosulfate enhanced visible light photocatalytic degradation bisphenol A by single-atom dispersed Ag mesoporous g-C₃N₄ hybrid[J]. Applied Catalysis B:Environmental, 2017,211:79-88.
[8] Yang S, Guo X, Wang Z, et al. Significance of B-site cobalt on bisphenol A degradation by MOFs-templated CoxFe_3−xO₄ catalysts and its severe attenuation by excessive cobalt-rich phase[J]. Chemical Engineering Journal, 2019,359:552-563.
[9] Zhou K, Zhu Y, Yang X, et al. Preparation of graphene-TiO₂ composites with enhanced photocatalytic activity[J]. New Journal of Chemistry, 2011,35(2):353-359.
[10] Wang L, Wen M, Wang W, et al. Photocatalytic degradation of organic pollutants using rGO supported TiO₂-CdS composite under visible light irradiation[J]. Journal of Alloys and Compounds, 2016,683:318-328.
[11] Yang Z, Qian J, Yu A, et al. Singlet oxygen mediated iron-based Fenton-like catalysis under nanoconfinement[J]. Proceedings of the National Academy of Sciences, 2019,116(14):6659-6664.
[12] Geng Y, Chen D, Li N, et al. Z-Scheme 2D2D α-Fe₂O₃g-C₃N₄ heterojunction for photocatalytic oxidation of nitric oxide[J]. Applied Catalysis B:Environmental, 2021,280:119409.
[13] Y Cong, X Li, Y Qin, et al. Carbon-doped TiO₂ coatingon multiwalled carbon nanotubes with higher visible light photocatalytic activity[J].Applied Catalysis B:Environmental, 2011,107:128-134.
[14] Y Li, Z Liu, Y Wu, et al. Carbon dots-TiO₂ nanosheets composites for photoreduction of Cr(VI) under sunlight illumination:Favorable roleof carbon dots[J]. Applied Catalysis B:Environmental, 2018,224:508-517.
[15] H Tan, Z Zhao, M Niu, et al. A facile and versatile method for preparation of colored TiO₂ with enhanced solar-driven photocatalytic activity[J]. Nanoscale, 2014,6:10216-10223.
[16] X Liu, Z Xing, Y Zhang, et al. Fabrication of 3D flower-like black N-TiO₂_-X@MoS₂ for unprecedented-high visible-light-driven photocatalytic performance[J]. Applied Catalysis B:Environmental, 2017,201:119-127.
[17] 许路.碳基催化剂活化过硫酸盐的有机物降解效能与机理研究[D]. 西安:西安建筑科技大学, 2020,001359:81-87. LU X.Study on the efficiency and mechanism of organic degradation by carbon-based catalysts via persulfate activation[D]. Xi'an:Xi'an University of Architecture and Technology, 2020,001359:81-87.
[18] Lu Z, Liu B, Dai W, et al. Carbon network framework derived iron-nitrogen co-doped carbon nanotubes for enhanced oxygen reduction reaction through metal salt-assisted polymer blowing strategy[J]. Applied Surface Science, 2019,463:767-774.
[19] Li X, Liu X, Lin C, et al. Catalytic oxidation of contaminants by Fe⁰ activated peroxymonosulfate process:Fe(IV) involvement, degradation intermediates and toxicity evaluation[J]. Chemical Engineering Journal, 2020,382:123013.
[20] Zhang Q, Liu N, Guan J. Charge-transfer effects in Fe-Co and Fe-Co-Y oxides for electrocatalytic water oxidation reaction[J]. ACS Applied Energy Materials, 2019,2(12):8903-8911.
[21] Xu L, Yang L, Bai X, et al. Persulfate activation towards organic decomposition and Cr(VI) reduction achieved by a novel CQDs-TiO_2−xrGO nanocomposite[J].Chemical Engineering Journal, 2019, 373:238-250.
[22] 颉亚玮,黄静杰,蒋毅恒,等.Fe/Ti-MIL-NH2吸附-光催化降解NDPhA[J]. 中国环境科学, 2022,42(4):1652-1662. Xie Y W, Huang J J, Jiang Y H, et al. Adsorption-photocatalysis for the removal of NDPhA by Fe/Ti-Mil-NH2[J]. China Environmental Science, 2022,42(4):1652-1662.
[23] 周爱娟,赵玉珏,刘芝宏,等.Fe(II)活化过硫酸盐处理喹啉工艺参数优化及生物毒性[J]. 中国环境科学, 2020,40(11):4795-4803. Zhou A J, Zhao Y J, Liu Z H, et al. Accelerated quinoline removal by Fe(II)-activated persulfate:parameters optimization and biological detoxification analysis[J]. China Environmental Science, 2020,40(11):4795-4803.
[24] Yang S, Wang P, Yang X, et al. Degradation efficiencies of azo dye Acid Orange 7by the interaction of heat, UV and anions with common oxidants:Persulfate, peroxymonosulfate and hydrogen peroxide[J]. Journal of Hazard Materials, 2010,179(1-3):552-558.
[25] Y Ma, B Wang, Q WANG, et al. Facile synthesis of α-FeOOHγ-Fe₂O₃ by a pH gradient method and the role of γ-Fe₂O₃ in H₂O₂ activation under visible light irradiation[J]. Chemical Engineering Journal, 2018, 354:75-84.
[26] Wang Y, Zhao X, Cao D, et al. Peroxymonosulfate enhanced visible light photocatalytic degradation bisphenol A by single-atom dispersed Ag mesoporous g-C₃N₄ hybrid[J]. Applied Catalysis B:Environmental, 2017,211:79-88.
[27] Lu Z, Zeng L, Song W, et al. In situ synthesis of C-TiO₂g-C₃N₄ heterojunction nanocomposite as highly visible light active photocatalyst originated from effective interfacial charge transfer[J]. Applied Catalysis B:Environmental, 2017,202:489-499.
[28] Yu L, Zhang X, Li G, et al. Highly efficient Bi₂O₂CO₃BiOCl photocatalyst based on heterojunction with enhanced dye-sensitization under visible light[J]. Applied Catalysis B:Environmental, 2016,187:301-309.
[29] Holm A, Hamandi M, Simonet F, et al. Impact of rutile and anatase phase on the photocatalytic decomposition of lactic acid[J]. Applied Catalysis B:Environmental, 2019,253:96-104.
[30] Anipsitakis G P, Dionysiou D D. Radical generation by the interaction of transition metals with common oxidants[J]. Environmental science & technology, 2004,38(13):3705-3712.
[31] Lu Xu, Siyu Cao, Xue Bai, et al. Efficient Fe(III) reduction and persulfate activation induced by ligand-to-metal charge transfer under visible light enhances degradation of organics[J]. Chemical Engineering Journal, 2022,46(2):216-218.
[32] Dong H, Zeng G, Tang L, et al. An overview on limitations of TiO₂-based particles for photocatalytic degradation of organic pollutants and the corresponding countermeasures[J]. Water Research, 2015,79:128-146.
[33] Ghauch A, Tuqan A M, Kibbi N, et al. Methylene blue discoloration by heated persulfate in aqueous solution[J]. Chemical Engineering Journal, 2012,213:259-271.
[34] Renli Yin, Yanxi Chen, Jiayue Hu, et al.Complexes of Fe(III)-organic pollutants that directly activate Fenton-like processes under visible light[J].Applied Catalysis B:Environmental, 2021,206.
[35] Tong Ren, Yulei Chi, Yu Wang, et al. Diversified metabolism makes novel Thauera strain highly competitive in low carbon wastewater treatment[J]. Water Research, 2021,206:117742.
[36] Zhuo-Yu Li, Lu Wang, Yu-Lei Liu, et al. Unraveling the interaction of hydroxylamine and Fe(III) in Fe(II)/Persulfate system:A kinetic and simulating study[J]. Water Research, 2020,168:115093.