Research on the preparation of ultrasonic-assisted ferric salts modified phosphorous slag and its As(Ⅲ) removing capacity |
WANG Cui-cui, CHEN Qiu-ling, LIU Shu-gen, HE Wen-hao, GAO Ye, NING Ping, GAO Hua-ping |
Faculty of Environmental Science and Engineering, Kunming University of Science and Technology, Kunming 650500, China |
|
|
Abstract The adsorption experiment of As(Ⅲ) in water was studied, and the ultrasonic-assisted ferric salts modified phosphorus slag for adsorbent was used. The effects of the variety and concentration of ferric salts, ultrasonic time in the process of modification on the adsorbing capacity for As(Ⅲ) by using modified phosphorous slag have been investigated. The optimal preparation conditions are as follows:0.8mol/L of FeCl3, and ultrasonic time of 15min. The methods FT-IR, SEM and XPS were used to analyze the difference of the modified and un-modified phosphorous slag. After modification, Fe3+ can be a very good load in the surface of phosphorus slag and the removal rate of As(Ⅲ) in wastewater was improved to 98.9%, compared with the unmodified, increased by 38%. The kinetics of adsorption process fitted in with pseudo second order reaction, the fitting correlation coefficient (R2) is above 0.96; The adsorption isotherm could also satisfy both isotherm model of Langmuir and Freundlich simultaneously, the fitting correlation coefficient (R2) is above 0.90. In comparison, the Langmuir isotherm model has a better description of the adsorption process.
|
Received: 24 October 2016
|
|
|
|
|
[1] |
李柏林,李晔,汪海涛,等.含砷废渣的固化处理[J]. 化工环保, 2008,28(6):153.
|
[2] |
Fendorf Scoot, Michael Holly A, van Geen Alexander. Spatial and Temporal Variations of Groundwater Arsenic in South and Southeast Asia[J]. Science, 2010,328(5982):1123-1127.
|
[3] |
韩子夜,蔡五田,张福存,等.国外高砷地下水研究现状及对我国高砷地下水调查工作的建议[J]. 水文地质工程地质, 2007, 34(3):126-128.
|
[4] |
U. S. EPA. National primary drinking water regulations:arsenic and clarifications to compliance and new source contaminants monitoring; final rule[J]. Federal Register, 2001,66(14):69-76.
|
[5] |
冯彦房,薛利红,杨梖,等.载镧生物炭的优化制备及其对水体中砷的吸附[J]. 中国环境科学, 2015,35(8):2433-2441.
|
[6] |
王琼,胡健,黄亚许,等.粉煤灰及其改性材料对废水中砷离子的吸附研究[J]. 矿冶, 2015,24(1):74-76.
|
[7] |
刘冬梅,方坤河,吴凤燕,等.磷渣开发利用的研究[J]. 矿业快报, 2005,21(3):21-25.
|
[8] |
朱建国,代玉林.贵州"十二五"磷化工产业基础与发展分析(上)[J]. 贵州化工, 2011,3:21-22.
|
[9] |
陶俊法.中国黄磷工业现状与发展前景[J]. 无机盐工业, 2008, 40(6):1-4.
|
[10] |
韩代水.利用黄磷渣生产磷渣超微粉用于水泥添加剂[J]. 磷肥与复肥, 2012,(4):72-73.
|
[11] |
殷飞.重金属复合污染土壤固定修复中钝化剂筛选及其作用机制[D]. 昆明:昆明理工大学, 2015.
|
[12] |
William T, Frankenberger J. Environmental Chemistry of Arenic[M]. USA:Marcel Dekker,Inc. 155-181.
|
[13] |
肖静.载铁活性炭吸附剂的制备及除砷机理研究[D]. 湘潭:湘潭大学, 2013.
|
[14] |
罗曼,关平,刘文汇.利用红外光谱鉴别饱和脂肪酸及其盐[J]. 光谱学与光谱分析, 2007,27(2):50-253.
|
[15] |
范伟,王亮,郑怀礼,等.基于红外光谱分析研究矿化剂对铝酸钙粉制备的影响[J]. 光谱学与光谱分析, 2015,35(5):1214-1217.
|
[16] |
李建军,刘晓伟,王岳,等.不同结晶程度SiO2的红外光谱特征及其意义[J]. 红外, 2010,31(12):31-35.
|
[17] |
朱多学.金属催化臭氧化催化剂的制备与性能研究[D]. 哈尔滨:哈尔滨工业大学, 2006.
|
[18] |
高守超,张康助,郭平军.钢与胶粘剂粘接界面的XPS分析[J]. 固体火箭技术, 2004,(2):154-156+164.
|
[19] |
Su C, Puls RW. Significance of iron(Ⅱ,Ⅲ) hydroxycarbonate green rust in arsenic remediation using zerovalent iron in laboratory column tests[J]. Environ.Sci.Technol., 2004,38(19):5224-5231.
|
[20] |
杨荣生,陈衍景,谢景林.甘肃阳山金矿床含砷黄铁矿及毒砂的XPS研究[J]. 岩石学报, 2009,11:2791-2800.
|
[21] |
梁美娜,朱义年,刘海玲,等.氢氧化铁对砷的吸附研究[J]. 水处理技术, 2006,32(7):32-37.
|
[22] |
孙福红,廖海清,陈艳卿,等.微囊藻对锑(V)生物吸附作用研究[J]. 中国环境科学, 2016,36(11):3383-3389.
|
[23] |
吕游.改性活性炭对含铜废水吸附性能及其机理研究[D]. 昆明:昆明理工大学, 2015.
|
[24] |
Tan A W, Hameed B H and Ahmad A L. Equilibrium and kinetic studies on basic dye adsorption by oil palm fibre activated carbon[J]. Chemical Engineering Journal, 2007,127:111-119.
|
[25] |
陈苹.载铁活性炭吸附材料的制备及对水中砷(Ⅴ)的吸附研究[D]. 赣州:江西理工大学, 2015.
|
|
|
|