Influence of metal cations on catalytic oxidation of NO over high-silica zeolites |
ZHOU Fei-xiang, WANG Jun, QIAN Ding-li, WU Xiang-hao, LIU Hua-yan, LU Han-feng |
State Key Laboratory Breeding Base of Green Chemistry-Synthesis Technology, College of Chemical Engineering, Zhejiang University of Technology, Hangzhou 310014, China |
|
|
Abstract A series of HZSM-5、Na-、K-、Co-、NiZSM-5catalysts were prepared by ion exchanged method and characterized by XRD、BET、ICP-MS and Py-IR. Their catalytic activities were investigated in the catalytic oxidation of NO. Results showed that the CoZSM-5possessed moderate surface acidity and was the most beneficial for NO oxidation, then performed highest activity to 47%. Meanwhile, the influences of space velocity, O2 concentration (5%~20%) and SO2 concentration (0~200×10-6) were investigated, under 600×10-6 inlet NO concentration and 100% RH. Experimental results revealed that SO2 concentration (below 200×10-6) had little impact on NO oxidation reaction and the NO oxidation conversion was maintained at 40% in 56h lifetime test, under 30℃、600ppm NO、18000h-1 SV and 100% RH.
|
Received: 18 September 2017
|
|
|
|
|
[1] |
张润铎,全燮,杨凤林,等.蜂窝状筛网催化剂上NH3催化还原NO[J]. 中国环境科学, 2002,22(1):20-23.
|
[2] |
谭青,冯雅晨.我国烟气脱硝行业现状与前景及SCR脱硝催化剂的研究进展[J]. 化工进展, 2011,(s1):709-713.
|
[3] |
张平,王乐夫,谭宇新.汽车尾气净化催化剂Ag-ZSM-5选择性催化还原NO[J]. 中国环境科学, 2002,23(4):293-296.
|
[4] |
乔南利,杨忆新,宋焕巧,等.低温NH3-SCR脱硝催化剂的研究现状与进展[J]. 化工环保, 2017,37(3):282-288.
|
[5] |
袁从慧,刘华彦,卢晗锋,等.催化氧化-碱液吸收脱除硝酸工业NOx 废气[J]. 化学反应工程与工艺, 2008,24(5):476-480.
|
[6] |
袁从慧,刘华彦,卢晗锋,等.催化氧化-还原吸收法脱除工业含湿废气中NOx[J]. 环境工程学报, 2008,2(9):1207-1212.
|
[7] |
任晓莉,张雪梅,张卫江,等.碱液吸收法治理含NOx 工艺尾气实验研究[J]. 化学工程, 2006,34(9):63-66.
|
[8] |
杨业,徐超群,朱燕群,等.臭氧氧化结合硫代硫酸钠溶液喷淋同时脱硫脱硝[J]. 化工学报, 2016,67(5):2041-2047.
|
[9] |
童志权,莫建红.催化氧化法去除烟气中NOx 的研究进展[J]. 化工环保, 2007,27(3):193-199.
|
[10] |
张瑞元,李凯,宁平,等.催化氧化法去除烟气中NOx 的研究现状与展望[J]. 材料导报, 2015,29(15):123-129.
|
[11] |
Shen Y, Ge X, Chen M. Catalytic oxidation of nitric oxide (NO) with carbonaceous materials[J]. RSC Advances, 2016,6(10):8469-8482.
|
[12] |
Guo Z, Xie Y, Hong I, et al. Catalytic oxidation of NO to NO2 on activated carbon[J]. Energy conversion and management, 2001, 42(15):2005-2018.
|
[13] |
Mochida I, Kisamori S, Hironaka M, et al. Oxidation of NO into NO2 over Active Carbon Fibers[J]. Energy & Fuels, 1994,8(6):611-624.
|
[14] |
刘鹤年,黄正宏,王明玺,等.常温下沥青基活性炭纤维对NO的催化氧化性能[J]. 化工学报, 2011,62(2):369-373.
|
[15] |
Chen H Y, Wei Z, Kollar M, et al. NO oxidation on zeolite supported Cu catalysts:Formation and reactivity of surface nitrates[J]. Catalysis Today, 2016,267:17-27.
|
[16] |
Akter N, Han L X, Huaman D, et al. NO and NH3 Oxidation over Zeolite Materials[J]. Materials Today:Proceedings, 2016,3(2):550-555.
|
[17] |
李玉芳,刘华彦,黄海凤,等.疏水型H-ZSM-5分子筛上NO氧化反应的研究[J]. 中国环境科学, 2009,29(5):469-473.
|
[18] |
钱定利,周飞翔,汪俊,等.silicalite-1全硅分子筛常温催化氧化NO性能[J]. 中国环境科学, 2017,37(6):2080-2086.
|
[19] |
刘华彦,李玉芳,徐媛媛,等.高硅ZSM-5分子筛表面NO常温氧化过程中的吸附与催化[J]. 高校化学工程学报, 2011,25(4):615-621.
|
[20] |
刘华彦,张泽凯,徐媛媛,等.高硅Na-ZSM-5分子筛表面NO的常温吸附-氧化机理[J]. 催化学报, 2010,31(10):1233-1241.
|
[21] |
李玉芳,刘华彦,黄海凤,等. NO在分子筛ZSM-5催化剂上催化氧化动力学研究[J]. 中国环境科学, 2010,30(2):161-166.
|
[22] |
Yuan C, Liu H, Zhang Z, et al. Alkali-metal-modified ZSM-5zeolites for improvement of catalytic dehydration of lactic acid to acrylic acid[J]. Chinese Journal of Catalysis, 2015,36(11):1861-1866.
|
[23] |
张文祥,贾明君,张春雷,等.不同母体制备的金属离子交换ZSM-5分子筛上C3H6选择催化还原NO反应的研究[J]. 中国环境科学, 1997,(6):504-507.
|
[24] |
李凤义,刘宗章,沈德建,等.镍改性HZSM-5催化乙醇脱水制备乙烯[J]. 现代化工, 2013,33(5):54-57.
|
[25] |
张文祥,贾明君,吴通好.金属离子交换分子筛的NO吸附性能[J]. 高等学校化学学报, 1997,18(12):1999-2003.
|
[26] |
张永春,薛全民,谭大志.钴离子改性的ZSM-5对低浓度NO吸附性能研究[J]. 大连理工大学学报, 2005,45(4):487-491.
|
[27] |
高月明,于庆君,易红宏,等. Cu-ZSM-5对燃气烟气中NO的吸附特性[J]. 中国环境科学, 2016,36(8):2275-2281.
|
[28] |
Hu H, Lyu J, Cen J, et al. Promoting effects of MgO and Pd modification on the catalytic performance of hierarchical porous ZSM-5for catalyzing benzene alkylation with methanol[J]. RSC Advances, 2015,5(77):63044-63049.
|
[29] |
Zhang R, Wang Z. Catalytic cracking of 1-butene to propylene by Ag modified HZSM-5[J]. Chinese Journal of Chemical Engineering, 2015,23(7):1131-1137.
|
[30] |
薛全民,张永春,宋伟杰.钴离子改性的Y型分子筛对低浓度NO吸附性能的研究[J]. 离子交换与吸附, 2004,20(3):254-259.
|
|
|
|