Properties and environmental impacts on repeated recycled aggregate concrete |
WANG Zhen-shuang1, SU Hao-lin2 |
1. School of Investment & Construction Management, Dongbei University of Finance and Economics, Dalian 116023, China;
2. School of Naval Architecture, Shanghai Jiaotong University, Shanghai 200240, China |
|
|
Abstract According to the cradle-to-gate life cycle evaluation method and taking into account the environmental impact distribution of concrete recycling, this research studies on properties and environmental impacts of repeated recycled aggregate concrete, and the optimum number of repeated regeneration of concrete is optimized on efficiency function method. The results concluded that, the slump, strength and electric flux decreased with cycles of repeated regeneration of concrete increasing, the 28d compressive strength 33.3MPa after 3repeated cycles, which arrived the design strength requirements. Compared with ordinary concrete, the slump decreased by 38.9% and electric flux increased by 85.7%, respectively; The ecological efficiency of concrete material increases with the repeated cycles increasing, the values of GWP, CED, and CMR of concrete materials are reduced with the increase of the repeated cycles increasing, The reduction variation from high to low is:CMR > GWP > CED; Taking into account the slump, the compressive strength, the electrical flux, the GWP, the CED, and the CMR in four concrete mix scenarios, the total efficiency coefficient of concrete from high to low is:the first generation recycled concrete > the second generation recycled concrete > the third generation recycled concrete > ordinary concrete.
|
Received: 20 June 2018
|
|
|
|
|
[1] |
杨桂权,阎慧群,郑祖成.再生混凝土应用优势与经济性分析[J]. 建筑经济, 2013,36(7):86-88.
|
[2] |
汪振双,赵宁,苏昊林.能源-经济-环境耦合协调度研究-以山东省水泥行业为例[J]. 软科学, 2015,29(2):33-36.
|
[3] |
王立久,汪振双,崔正龙.基于冻融损伤抛物线模型的再生混凝土寿命预测[J]. 应用基础与工程科学学报, 2011,19(1):29-35.
|
[4] |
汪振双,宁欣,赵一健.基于价值工程原理的混凝土物化阶段碳排放评价[J]. 硅酸盐通报, 2016,35(12):4308-4313.
|
[5] |
汪振双,王宝民,苏昊林,等.橡胶颗粒对再生混凝土耐久性影响[J]. 哈尔滨工业大学学报, 2015,47(6):109-112.
|
[6] |
Zhenshuang W, Lijiu W, Zhenglong C, et al. Recycled coarse aggregate on concrete compressive strength[J]. Transactions of Tianjin University, 2011,17(3):229-234.
|
[7] |
Butler L, West J S, Tighe S L. The effect of recycled concrete aggregate properties on the bond strength between RCA concrete and steel reinforcement[J]. Cement and Concrete Research, 2011,41(10):1037-1049.
|
[8] |
Eduardus A B, Koenders, M P. Compressive strength and hydration processes of concrete with recycled aggregates[J]. Cement and Concrete Research, 2014,56:203-212.
|
[9] |
Panda K C, Bal P K. Properties of Self Compacting Concrete Using Recycled Coarse Aggregate[J]. Procedia Engineering, 2013,51:159-164.
|
[10] |
Sumaiya B H M, Shahria A. Mechanical behavior of three generations of 100% repeated recycled coarse aggregate concrete[J]. Construction and Building Materials, 2014,65:574-582.
|
[11] |
孙杰,胡思为,杨静.废弃混凝土循环利用的研究[J]. 建材世界, 2016,37(2):32-35.
|
[12] |
ISO 14040-2000 Environmental Management-Life Cycle Assess-Principles and Framework[S].
|
[13] |
Chen C, Habert G, Bouzidi Y, et al. LCA allocation procedure used as an incitative method for waste recycling:An application to mineral additions in concrete[J]. Resources Conservation and Recycling, 2010,54(12):1231-1240.
|
[14] |
章玉容.粉煤灰混凝土生命周期环境影响综合评价[D]. 北京:北京交通大学博士学位论文, 2016.
|
[15] |
尹健,邹伟,池漪.高性能再生混凝土环境协调性评价[J]. 铁道科学与工程学报, 2011,8(5):19-25.
|
[16] |
Carmine L, Antonio C, Ciro F, et al. Physical properties and mechanical behaviour of concrete made with recycled aggregates and fly ash[J]. Construction and Building Materials, 2013,47:547-559.
|
[17] |
JGJ52-2006普通混凝土用砂、石质量及检验方法标准[S].
|
[18] |
GB/T 25177-2010混凝土用再生粗骨料[S].
|
[19] |
李小冬,王帅,孔祥勤,等.预拌混凝土生命周期环境影响评价[J]. 土木工程学报, 2011,44(1):132-138.
|
[20] |
GB/T50080-2002普通混凝土拌合物性能试验方法[S].
|
[21] |
GB/T50081-2002普通混凝土力学性能试验方法[S].
|
[22] |
ASTM C 1202-2010 Stand test method for electrical indication of concrete's ability to resist chloride ion penetration[S].
|
[23] |
张海涛,王如松,胡聃,等.煤矿固废资源化利用的生态效率与碳减排-以淮北市为例[J]. 生态学报, 2011,31(19):5638-5645.
|
[24] |
汪振双,赵宁.基于功效函数法的我国房地产企业竞争力评价[J]. 工程管理学报, 2014,28(4):143-147.
|
[25] |
汪振双,周梅.基于价值工程原理的煤矸石混凝土配合比设计方案选择[J]. 数学的实践与认识, 2015,45(7):126-131.
|
[26] |
魏军晓,耿元波,沈镭,等.基于国内水泥生产现状的碳排放因子测算[J]. 中国环境科学, 2014,34(11):2970-2975.
|
[27] |
李文贵.再生骨料混凝土破坏机理与改性研究综述[J]. 建筑科学与工程学报, 2016,33(6):60-72.
|
[28] |
郭远新.再生细骨料强化技术对其性能的影响[J]. 混凝土, 2015, (4):95-98.
|
[29] |
殷仁述,杨沿平,杨阳,等.车用钛酸锂电池生命周期评价[J]. 中国环境科学, 2018,38(6):2371-2381.
|
[30] |
汪振双,赵宁.基于功效函数法的储能砂浆相变材料用量优化[J]. 数学的实践与认识, 2015,45(8):128-135.
|
|
|
|