Response surface method optimization of preparation fly ash based polysilicate aluminum chloride coagulant: performance and microstructure characterization |
LAO De-ping1, DING Shu-qiang2, NI Wen1, LI Xiao-guang2, LI Jia-jie1, GAO Guang-hui2 |
1. School of Civil and Resource Engineering, University of Science and Technology Beijing, Beijing 100083, China;
2. National Institute of Clean and Low Carbon Energy, Beijing 102211, China |
|
|
Abstract This paper investigates the factors that influence the preparation of polysilicate aluminum chloride coagulant using coal fly ash and their performance and microstructure. Four factors(basicity, n(Si):n(Al), polymerization temperature and reaction time) and three levels of response surface experiments were carried out, which regarded the transmittance of Kaolin simulated wastewater as the evaluation index. Results show that the optimum scheme when the basicity was 1.18, the n(Si):n(Al) was 5.64, the polymerization temperature was 47.40℃, and the reaction time was 2.48 hours. At the optimum theme, the predicted value of transmittance reaches 86.58%, the relative error of all the verification experiments was 0.18%, and the correlation coefficient of the model is 0.9984, which indicated the RSM optimization model is reliable. The performance of coagulant increases continuously with the increase of dosage, and tends to be stable eventually. With the increase of pH of wastewater, it increases first and then decreases. X-ray diffraction test indicates the formation of sodium chloride and new amorphous polymers which through the polymerization reaction of fly ash leachate and polysilicic acid. The infrared tests illustrates that a large amount of nonionic complex state (such as metal-hydroxyl groups) occurs between polysilicate acid and Al3+ and it's hydrolysate. The SEM micrograph shows that the product presents a three-dimensional reticular structure, with high level of aggregation and branches.
|
Received: 11 May 2018
|
|
|
|
|
[1] |
赵蕾,代世峰,张勇,等.内蒙古准格尔燃煤电厂高铝粉煤灰的矿物组成与特征[J]. 煤炭学报, 2008,33(10):1168-1172.
|
[2] |
杨静,蒋周青,马鸿文,等.中国铝资源与高铝粉煤灰提取氧化铝研究进展[J]. 地学前缘, 2014,21(5):313-324.
|
[3] |
梁振凯,雷雪飞,孙应龙,等.氯化钙焙烧法提取粉煤灰中的氧化铝[J]. 中国环境科学, 2013,33(9):1601-1606.
|
[4] |
Blissett R S, Rowson N A. A review of the multi-component utilisation of coal fly ash[J]. Fuel, 2012,97:1-23.
|
[5] |
Yao Z T, Xia M S, Sarker P, et al.A review of the alumina recovery from coal fly ash, with a focus in China[J]. Fuel, 2014,120:74-85.
|
[6] |
张开仕,曾凤春.利用工业废弃物制备聚合硫酸铁铝硅混凝剂[J]. 化工学报, 2008,59(9):2361-2365.
|
[7] |
张琼,李国斌,苏毅,等.复合聚硅酸铝铁絮凝剂的形貌结构及性能研究[J]. 非金属矿, 2015,38(1):1-4.
|
[8] |
熊丽丽,高丽,秦冬玲,等.PSAF-PD絮凝剂的研制及在造纸废水中的应用[J]. 现代化工, 2016,36(9):104-108.
|
[9] |
王社宁,席启斐,常青,等.响应面法优化沸石协同CSAX混凝消除含锌废水中的Zn2+[J]. 中国环境科学, 2016,36(11):3335-3340.
|
[10] |
杜凤龄,王刚,徐敏,等.新型高分子螯合-絮凝剂制备条件的响应面法优化[J]. 中国环境科学, 2015,35(4):1116-1122.
|
[11] |
徐向宏,何明珠.试验设计与Design-Expert,SPSS应用[M]. 北京:科学出版社, 2010:146-160.
|
[12] |
邢奕,王志强,洪晨,等.基于RSM模型对污泥联合调理的参数优化[J]. 中国环境科学, 2014,34(11):2866-2873.
|
[13] |
刘静,苏秀霞,崔明.响应面优化β-环糊精对工业骨胶的除臭工艺[J]. 化工进展, 2017,36(7):2615-2620.
|
[14] |
王鹏,魏徳洲.响应曲面法优化氨法焙烧后粉煤灰除铁工艺[J]. 东北大学学报(自然科学版), 2014,35(11):1617-1621.
|
[15] |
Yuan H P, Zhu N W, Song L J. Conditioning of sewage sludge with electrolysis:Effectiveness and optimizing study to improve dewaterability[J]. Bioresource Technology, 2010,101:4285-4290.
|
[16] |
曹百川,高宝玉,岳钦艳,等.聚合硅酸硫酸铁和聚合硫酸铁处理黄河水的效果及其絮体特性研究[J]. 中国科学:化学, 2010,40(4):399-406.
|
[17] |
闵凡飞,赵晴,李宏亮,等.煤泥水中高岭土颗粒表面荷电特性研究[J]. 中国矿业大学学报, 2013,42(2):284-290.
|
[18] |
吴敏,崔秀云,苗茂栋.zeta电位与菌悬液絮凝活性[J]. 化工学报, 2008,59(9):2263-2269.
|
[19] |
许友泽,成应向,付广义,等.PSAF-DMDAAC复合絮凝剂的制备及含铊废水的处理[J]. 化工环保, 2017,37(1):62-67.
|
[20] |
张琼,黄晓梅,李国斌,等.聚硅酸铝铁絮凝剂处理云南滇池污染水的应用研究[J]. 水处理技术, 2015,41(2):80-84.
|
[21] |
陈凌,沙琳,张正红,等.聚硅酸铝铁(Ⅱ)镁混凝剂的制备及其对印染废水的处理[J]. 水处理技术, 2011,37(12):42-50.
|
[22] |
王爱民,白妮,王金玺,等.粉煤灰聚硅酸铝铁絮凝剂的制备及处理洗煤废水研究[J]. 离子交换与吸附, 2017,33(4):350-360.
|
[23] |
张垒,王凯军,刘霞,等.PFS混凝-光催化氧化深度处理焦化废水试验研究[J]. 现代化工, 2014,34(7):77-80.
|
[24] |
苗晶,岳钦艳,高宝玉.高浓聚合氯化铁混凝剂的制备及其混凝效果研究[J]. 工业水处理, 2002,22(8):22-25.
|
[25] |
鞠佳伟,高玉萍,何赞,等.pH对铝盐絮凝剂形态分布与混凝除氟性能的影响[J]. 环境工程学报, 2015,9(6):2563-2568.
|
[26] |
欧文波,祝方,贾文珍,等.壳聚糖改性高分子絮凝剂对焦化废水Zeta电位的影响研究[J]. 工业安全与环保, 2015,41(2):4-12.
|
[27] |
晏井春,闫永胜,朱富坤,等.纳米聚硅氯化铝复合絮凝剂的制备、表征与应用研究[J]. 净水技术, 2008,27(2):57-61.
|
[28] |
高宝玉,岳钦艳,王燕,等.复合高分子絮凝剂[M]. 北京:化学工业出版社, 2016:22-23,75-77.
|
[29] |
张开仕,曾凤春,谭超,等.聚合硅酸硫酸铁铝混凝剂的制备表征与混凝性能[J]. 化工学报, 2013,64(8):3070-3075.
|
[30] |
范剑明,吉仁塔布,李诚诚,等.聚硅酸铝铁絮凝剂的制备及其性能研究[J]. 矿产保护与利用, 2012,4:37-40.
|
[31] |
刘智安,王娜,刘启旺,等.不同Fe3+/Al3+比复合阳离子絮凝剂聚合硫酸铝铁的合成及性能研究[J]. 中国电机工程学报, 2011, 31(5):90-95.
|
[32] |
Sun T, Sun C H, Zhu G L, et al. Preparation and coagulation performance of poly-ferric-aluminum-silicate-sulfate from fly ash[J]. Desalination, 2011,268:270-275.
|
[33] |
He L L, Xu X Y. Polymeric Aluminum Ferric Chloride Calcium Composite Flocculant:Preparation, Characteristics and Coagulation Performance[C]. International Conference on Frontiers of Environment, Energy and Bioscience, 2013:734-740.
|
[34] |
方月梅,赵旭德,张晓玲.复合絮凝剂聚硅酸铝铁的形貌结构及性能研究[J]. 工业安全与环保, 2007,33(10):22-24.
|
[35] |
付英,高宝玉.聚硅酸铁对溶解性有机物与浊度的去除[J]. 中国石油大学学报(自然科学版), 2010,34(1):134-138.
|
|
|
|