吡啶环改性石墨相氮化碳光催化还原Cr(VI)的研究

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (1121 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract In this paper, melamine and pyridine dicarboxylic acid were used to synthesis organic macromolecule precursors by hydrothermal synthesis, and graphitic carbon nitride (x% py-CN) modified with pyridine was designed. The x% py-CN catalysts were characterized by TEM, XRD, XPS, FT-IR and EIS. The photocatalytic reduction performance of x% py-CN catalyst was investigated by using Cr(VI) as the target pollutant. The results showed that 10% Py-CN had the best photocatalytic performance under simulated sunlight, and the photocatalytic reduction rate of 15mg/L Cr(VI) reached 85% under 3h irradiation. The improvement of the photocatalytic activity of catalysts was attributed to the fact that the modification of pyridine could effectively improve the separation efficiency of photogenerated electron hole pairs. In addition, the repeated cycle experiment showed that the catalyst has good stability and recycling ability, and had a good application prospect.

Key words： graphitic carbon nitride photocatalysis Cr(VI) pyridine modification

Received: 06 December 2021

PACS:

X703.1

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LIU Fang-yuan
	LIU Ya-nan
	LU Shuai-shuai
	CHEN Huan
	JIANG Fang

Cite this article:

LIU Fang-yuan,LIU Ya-nan,LU Shuai-shuai等. Photocatalytic reduction of Cr(VI) by pyridine doped graphitic carbon nitride[J]. CHINA ENVIRONMENTAL SCIENCECE, 2022, 42(7): 3130-3139.

URL:

http://www.zghjkx.com.cn/EN/ OR http://www.zghjkx.com.cn/EN/Y2022/V42/I7/3130

[1]	李承献,邵洪源.含铬废水净化研究进展[J].明胶科学与技术, 2015,35(2):55-62. Li C X, Shao H Y. Situation and Prospect on the processing craft for Cr (Ⅵ)[J]. The Science and Technology of Gelatin, 2015,35(2):55-62.
[2]	江芳,郑寿荣,郑正,等.SO42-/TiO2光催化还原Cr ()Ⅵ的研究[J].环境化学, 2005,24(4):389-393. Jiang F, Zhen S R, Zhen Z, et al. Study on photo-reduction of Cr (Ⅵ) catalyzed by SO24-/TiO2[J]. Environmental Chemistry, 2005,24(4):389-393.
[3]	Hasija V, Raizada P, et al. Progress on the photocatalytic reduction of hexavalent Cr (VI) using engineered graphitic carbon nitride[J]. Process Safety and Environmental Protection, 2021,152:663-678.
[4]	胡啸龙,孟昭福,王新欣,等.双子型复配增强两性膨润土吸附Cr (VI)的效应[J].中国环境科学, 2020,40(5):2087-2094. Hu X L, Meng F Z, Wang X X, et al. Enhancing effect of gemini surfactant complex modification on Cr (VI) adsorption by amphoteric bentonite[J]. China Environmental Science, 2020,40(5):2087-2094.
[5]	胡艺泓,黄廷林,孙远奎.硫酸根离子强化零价铁去除Cr (Ⅵ)的试验研究[J].中国环境科学, 2018,38(4):1318-1323. Hu Y H, Huang T L, Sun Y K. Enhanced chromium removal by zerovalent iron with the presence of sulfate anion[J]. China Environmental Science, 2018,38(4):1318-1323.
[6]	Yuan G, Li F, Li K, et al. Research progress on photocatalytic reduction of Cr (VI) in polluted water[J]. Bulletin of the Chemical Society of Japan, 2020,94(4):1142-1155.
[7]	Ong W J, Tan L L, Ng Y H, et al. Graphitic carbon nitride (g-C3N4)-based photocatalysts for artificial photosynthesis and environmental remediation:are we a step closer to achieving sustainability[J]. Chemical Reviews, 2016,116(12):7159-7329.
[8]	Wang Z, Chen M, Yu H, et al. Self-assembly synthesis of borondoped graphitic carbon nitride hollow tubes for enhanced photocatalytic NOx removal under visible light[J]. Applied Catalysis B Environmental, 2018,239:352-361.
[9]	Zhang L, Long R, Zhang Y, et al. Direct observation of dynamic bond evolution in single-atom Pt/C3N4catalysts[J]. Angewandte Chemie International Edition, 2020,59(15):6224-6229.
[10]	Jiang Z, Zhang X, Chen H, et al. Fusiform-shaped g-C3N4capsules with superior photocatalytic activity[J]. Small, 2020,16(42):2003910.
[11]	李冬梅,卢文聪,梁奕聪,等.Bi5O7I/g-C3N4Z型异质结的常温沉淀制备及其光催化性能研究[J].中国环境科学, 2021,41(9):4120-4126. Li D M, Lu W C, Liang Y C, et al. Room-temperature precipitation synthesis and photocatalysis of Bi5O7I/g-C3N4Z-scheme heterojunction[J]. China Environmental Science, 2021,41(9):4120-4126.
[12]	Lv H, Huang Y, Koodali R T, et al. Synthesis of sulfur-doped 2D graphitic carbon nitride nanosheets for efficient photocatalytic degradation of phenol and hydrogen evolution[J]. ACS Applied Materials&Interfaces, 2020,12(11):12656-12667.
[13]	Chen Z, Sun P, Fan B, et al. Textural and electronic structure engineering of carbon nitride via doping with π-deficient aromatic pyridine ring for improving photocatalytic activity[J]. Applied Catalysis B:Environmental, 2015,170-171:10-16.
[14]	Kumar P, Vahidzadeh E, Thakur U K, et al. C3N5:A low bandgap semiconductor containing an azo-linked carbon nitride framework for photocatalytic, photovoltaic and adsorbent applications[J]. Journal of the American Chemical Society, 2019,141(13):5415-5436.
[15]	Zhao C, Li Q, Xie Y, et al.Three-dimensional assemblies of carbon nitride tubes as nanoreactors for enhanced photocatalytic hydrogen production[J]. Journal of Materials Chemistry A, 2020,8:305-312.
[16]	Wen J, Xie J, Chen X, et al. A review on g-C3N4-based photocatalyst[J]. Applied Surface Science, 2017,391:72-123.
[17]	Li J, Wu D, Iocozzia J, et al. Achieving eEfficient incorporation of π-electrons into graphitic carbon nitride for markedly improved hydrogen generation[J]. Angewandte Chemie International Edition, 2019,58:1985-1989.
[18]	Ho W, Zhang Z, Lin W, et al. Copolymerization with 2,4,6-triaminopyrimidine for the rolling-up the layer structure, tunable electronic properties, and photocatalysis of g-C3N4[J]. ACS Applied Materials&Interfaces, 2015,7(9):5497-5505.
[19]	Lv Q, Cao C, Li C, et al. Formation of crystalline carbon nitride powder by a mild solvothermal method[J]. Journal of Materials Chemistry, 2003,13(6):1241-1243.
[20]	Dong H, Zhang X, Li J, et al. Construction of morphology-controlled nonmetal 2D/3D homojunction towards enhancing photocatalytic activity and mechanism insight[J]. Applied Catalysis B:Environmental, 2020,263:118270.
[21]	Gu J, Chen H, Jiang F, et al. Visible light photocatalytic mineralization of bisphenol a by carbon and oxygen dual-doped graphitic carbon nitride[J]. Journal of Colloid and Interface Science, 2019,540:97-106.
[22]	Qiu P, Xu C, Chen H, et al. One step synthesis of oxygen doped porous graphitic carbon nitride with remarkable improvement of photo-oxidation activity:role of oxygen on visible light photocatalytic activity[J]. Applied Catalysis B:Environmental, 2017,206:319-327.
[23]	Guo Q X, Xie Y, Wang X J, et al. Synthesis of carbon nitride nanotubes with the C3N4 stoichioetry via a benzene-thermal process at low temperatures[J]. Chemical Communications, 2004,1:26-27.
[24]	Fu Y, Zhu J, Hu C, et al. Covalently coupled hybrid of graphitic carbon nitride with reduced graphene oxide as a superior performance lithium-ion battery anode[J]. Nanoscale, 2014,6(21):12555-12564.
[25]	Chen J, Fu X, Chen H, et al. Simultaneous Gd2O3 clusters decoration and O-doping of g-C3N4 by solvothermal-polycondensation method for reinforced photocatalytic activity towards sulfamerazine[J]. Journal of Hazardous Materials, 2021,402:123780.
[26]	Nguyen T B, Huang C P, Doong R A. Photocatalytic degradation of bisphenol a over a ZnFe2O4/TiO2 nanocomposite under visible light[J]. Science of The Total Environment, 2019,646:745-756.
[27]	Zhang J, Zhang X, Zhou T, et al. Photocatalytic removal of hexavalent chromium by Fe doped g-C3N4 loaded with dispersed diatomite modified by electron beam bombardment[J]. Journal of Cleaner Production, 2021,315:128219.
[28]	Wei L, Tian J, Wang Q, et al. A study on the mechanism and kinetic of nitrate reduction by the nZVI-g-C3N4/TiO2 composite under the simulated sunlight[J]. Journal of Materials Science:Materials in Electronics, 2021,32:15864-15881.
[29]	Bai Y, Wang T, Zhao X, et al. Synthesis of novel ternary Bi2WO6/CeO2/g-C3N4 composites with enhanced visible light photocatalytic activity for removal of organic and Cr (VI) from wastewater[J]. Journal of Materials Science:Materials in Electronics, 2020,31:17524-17534.
[30]	Zhang Y, Yang X, Wang Y, et al. Insight into L-cysteine-assisted growth of Cu2S nanoparticles on exfoliated MoS2nanosheets for effective photoreduction removal of Cr (VI)[J]. Applied Surface Science, 2020,518:146191.
[31]	Chen C, Zeng H, Xiong J, et al. Z-scheme AgBr@Ag/CoAl layered double hydroxide heterojunction for superior photocatalytic Cr (VI) reduction under visible light[J]. Applied Clay Science, 2020,192:105627.
[32]	Zhao X, Du P, Cai Z, et al. Photocatalysis of bisphenol a by an easy-settling titania/titanate composite:effects of water chemistryfactors, degradation pathway and theoretical calculation[J]. Environmental Pollution, 2018,232:580-590.
[33]	Tang Y, Yin X, Mu M, et al. Anatase TiO2@MIL-101(Cr) nanocomposite for photocatalytic degradation of bisphenol A[J]. Colloids and Surfaces A:Physicochemical and Engineering Aspects, 2020,596:124745.
[34]	Zhou Q, Li Y, Yang H, et al. A collaborative strategy for enhanced reduction of Cr () by Fe (0) in the presence of oxalate under sunlight:Ⅵ Performance and mechanism[J]. Journal of Environmental Sciences, 2020,90:388-397.
[35]	Li Q, Zhang L, Liu J, et al. Porous Carbon Nitride Thin Strip:Precise Carbon Doping Regulating Delocalized π Electron Induces Elevated-Photocatalytic Hydrogen Evolution[J]. Small, 2021,17(11):2006622.