烧结升温方式及气氛对水洗焚烧飞灰晶体演变的影响

朱芬芬; 柳晓燕; 韩媚玲; 高冈昌辉; 大下和徹; 董仪

PDF(1111 KB)

中国环境科学 ›› 2019, Vol. 39 ›› Issue (10) : 4212-4220.

固体废物

烧结升温方式及气氛对水洗焚烧飞灰晶体演变的影响

朱芬芬¹, 柳晓燕¹, 韩媚玲¹, 高冈昌辉², 大下和徹², 董仪¹

作者信息 +

Effect of heating program and atmosphere on the evolution of crystal washed fly ash during calcination

ZHU Fen-fen¹, LIU Xiao-yan¹, HAN Mei-ling¹, Takaoka Masaki², Oshita Kazuyuki², DONG Yi¹

Author information +

文章历史 +

摘要

为使水洗焚烧飞灰的稳定化处理进一步优化，探讨了热处理的加热过程、气氛条件等对水洗焚烧飞灰晶体成分演变的影响.同时也探讨了3种飞灰：锅炉飞灰（RFA）、CaO/Ca（OH）₂和NaHCO₃分别作为中和剂得到的两种飞灰（CaFA和NaFA）水洗后（RFA-II#、CaFA-II#和NaFA-II#）进行热处理比较.结果发现700℃是个转折点，从这个温度点开始3种水洗飞灰中的晶体成分发生明显变化；原位连续加热模式更容易形成固体溶液因而更适合重金属的稳定；NaFA-II#较之CaFA-II#更易于稳定重金属成分.Factsage的模拟结果与XRD结果一致，而且发现飞灰中氯化物在加热过程中首先释放的是HCl.

Abstract

In order to optimize the stabilization of washed municipal solid waste incineration (MSWI) fly ash (FA) by calcination, the influence of the heating method (continued-heating, multistep-heating) and atmosphere conditions on the evolution of crystal composition in washed FA was discussed. Three kinds of FA (RFA-II#、CaFA-II# and NaFA-II#) were tested and compared. RFA was the boiler fly ash (RFA), CaFA and NaFA were FA resulted from discharged gas neutralized by CaO/Ca(OH)₂ and NaHCO₃ respectively, and "II#" means they were dried residues treated by a double washing process. The results indicate that continued-heating was easier to form solid solution to stabilize heavy metals, and 700℃ was the turning point after which the crystal in three FAs changed obviously. The FA neutralized by NaHCO₃ was better to stabilize heavy metals. The simulation results from Factsage were consistent with the XRD results, and it was found that HCl was the first evaporation chloride released from the washed FA during the calcination process.

导出引用

朱芬芬, 柳晓燕, 韩媚玲, 高冈昌辉, 大下和徹, 董仪. 烧结升温方式及气氛对水洗焚烧飞灰晶体演变的影响[J]. 中国环境科学. 2019, 39(10): 4212-4220

ZHU Fen-fen, LIU Xiao-yan, HAN Mei-ling, Takaoka Masaki, Oshita Kazuyuki, DONG Yi. Effect of heating program and atmosphere on the evolution of crystal washed fly ash during calcination[J]. China Environmental Science. 2019, 39(10): 4212-4220

中图分类号： X705

参考文献

[1] 国家统计局.中国统计年鉴[J]. 北京:中国统计出版社, 2006-2017. National Bureau of Statistics of China. China Statistical Yearbook[J]. Beijing:China Statistical Press, 2006-2017.
[2] GB18485-2014《生活垃圾焚烧污染控制标准》[S]. GB18485-2014《Standard for pollution control on the municipal solid waste incineration》[S].
[3] 李军辉,吴新,刘道洁,等.不同处理方法对硅灰稳固化垃圾焚烧飞灰重金属的影响[J]. 中国环境科学, 2018,38(11):4198-4204. Li J H, Wi X, Liu D J, et al. Effects of different treatment methods on the stabilization of heavy metals in municipal solid waste incineration fly ash using silica fume[J]. China Environmental Science, 2018, 38(11):4198-4204.
[4] 李建陶,曾鸣,杜兵,等.垃圾焚烧飞灰药剂稳定化矿物学特性[J]. 中国环境科学, 2017,37(11):4188-4194. Li J T, Zeng M, Du B, et al. Mineralogical characteristics of MSWI fly ash stabilized by chemical reagents. China Environmental Science, 2017,37(11):4188-4194.
[5] Zhang FS, Itoh H. Extraction of metals from municipal solid waste incinerator fly ash by hydrothermal process[J]. Journal of Hazardous Materials, 2006,136:663-670.
[6] Karlfeldt K, Steenari B M. Assessment of metal mobility in MSW incineration ashes using water as the reagent[J]. Fuel, 2007,86:1983-1993.
[7] 叶暾旻,王伟,高兴保,等.我国垃圾焚烧飞灰性质及其重金属浸出特性分析[J]. 环境科学, 2007,28(11):2646-2650. Ye T M, Wang W, Gao X B, et al. Characterization and Heavy Metals Leaching Toxicity of Fly Ash from Municipal Solid Waste Incinerators in China[J]. Environmental Science, 2007,28(11):2646-2650.
[8] Derie R. A new way to stabilize fly ash from municipal incinerators[J]. Waste Management, 1996,16(8):711-716.
[9] Wang K S, Chiang K Y, Lin K L, et al. Effects of a water-extraction process on heavy metal behavior in municipal solid waste incinerator fly ash[J]. Hydrometallurgy, 2001,62:73-81.
[10] Jiang Y, Xi B, Li X, et al. Effect of water-extraction on characteristics of melting and solidification of fly ash from municipal solid waste incinerator[J]. Journal of Hazardous Materials, 2009,161:871-877.
[11] Chiang K Y, Hu Y H. Water washing effects on metals emission reduction during municipal solid waste incinerator (MSWI) fly ash melting process[J]. Waste Management, 2010,30(5):831-838.
[12] Chen W S, Chang F C, Shen Y H, et al. Removal of chloride from MSWI fly ash[J]. Journal of Hazardous Materials, 2012,237-238:116-120.
[13] Zhu F F, Takaoka M, Oshita K, et al. Chloride behavior in washing experiments of two kinds of municipal solid waste incinerator fly ash with different alkaline reagents[J]. Journal of the Air & Waste Management Association, 2009,59(2):139-147.
[14] Zhu F F, Takaoka M, Shiota K, et al. Chloride chemical form in various types of fly ash[J]. Environmental Science & Technology, 2008,42(11):3932-3937.
[15] Zhu F F, Takaoka M, Oshita K, et al. Comparison of two types of municipal solid waste incinerator fly ashes with different alkaline reagents in washing experiments[J]. Waste Management, 2009,29(1):259-264.
[16] Mangialardi T. Sintering of MSW fly ash for reuse as a concrete aggregate[J]. Journal of Hazardous Materials, 2001,B87:225-239.
[17] 李润东,于清航,李彦龙,等.烧结条件对焚烧飞灰烧结特性的影响研究[J]. 安全与环境学报, 2008,8(3):60-63. Li R D, Yu Q H, Li Y L, et al. Effect of experimental condition on sintering characteristics of MSWI fly ashes[J]. Journal of Safety and Environment, 2008,8(3):60-63.
[18] 王雷,金宜英,聂永丰,等.垃圾焚烧飞灰烧结特性[J]. 环境工程, 2009,27(S1):406-411. Wang L, Jin Y Y, Nie Y F, et al. Sintering characteristic of municipal solid waste incineration fly ash[J]. Environmental Engineering, 2009,27(S1):406-411.
[19] Lin K L. Feasibility study of using brick made from municipal solid waste incinerator fly ash slag[J]. Journal of Hazardous Materials, 2006,B137:1810-1816.
[20] Chou S Y, Lo S L, Hsieh C H, et al. Sintering of MSWI fly ash by microwave energy[J]. Journal of Hazardous Materials, 2009,163:357-362.
[21] Ponsot I, Bernardo E, Bontempi E et al. Recycling of pre-stabilized municipal waste incinerator fly ash and soda-lime glass into sintered glass-ceramics[J]. Journal of Cleaner Production, 2015,89:224-230.
[22] Liu Y, Zheng L, Li X, et al. SEM/EDS and XRD characterization of raw and washed MSWI fly ash sintered at different temperatures[J]. Journal of Hazardous Materials, 2009,162(1):161-173.
[23] Mu Y, Saffarzadeh A, Shimaoka T. Influence of ignition process on mineral phase transformation in municipal solid waste incineration (MSWI) fly ash:Implications for estimating loss-on-ignition (LOI)[J]. Waste Management, 2017,59:222-228.
[24] Zhu F F, Xiong Y Q, Wang Y Y, et al. Heavy metal behavior in "Washing-Calcination-Changing with Bottom Ash" system for recycling of four types of fly ashes[J]. Waste Management, 2018,75:216-225.