Tix-Ni1-x-MOFs的制备及其CO选择性催化还原NOx研究

摘要
图/表
参考文献
相关文章 (5)

全文: PDF (1563 KB) HTML (1 KB)
输出: BibTeX | EndNote (RIS)

摘要采用溶剂热法和微波法合成了不同比例的Ti_x-Ni_1-x-MOFs材料,并用于以CO为还原剂的选择性催化脱硝反应。结果表明,双金属Ti_x-Ni_1-_x-MOFs的NO还原率显著高于单金属Ni-MOF,且反应温度窗口更宽,其中,Ti_0.2-Ni_0.8-MOF表现出最佳的脱硝效率,在200~400^oC温度范围达到100%的转化率。通过XRD,FT-IR,SEM,TGA,XPS,N₂吸脱附等表征手段发现,Ti掺杂Ni-MOF后有利于改善原子分散性,Ti、Ni间金属的相互作用有利于产生丰富的高效Ni-O-Ti位点,加强Ni²⁺+Ti⁴⁺↔Ni³⁺+Ti³⁺氧化还原循环,从而明显提高了NO+CO催化反应性能。与溶剂热法相比,微波法制备Ti_0.2-Ni_0.8-MOF具有合成效率高、结晶度好、晶粒细小均匀的优势,并进一步提高了其低温脱硝效果。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	石勇
	李橙
	黄磊
	熊巍
	肇启东
	孙健恒
	丁越

关键词 ： CO-SCR, 金属有机骨架, Ti_x-Ni_1-x-MOFs, 微波法, 溶剂热法

Abstract：Ti_x-Ni_1-x-MOFs catalysts with different proportions were successfully synthesized by solvothermal method and microwave method, applied for selective catalytic reduction reaction of NO_x with CO. The doping of Ti significantly improved NO_x reduction performance of Ni-MOF catalysts and widened reaction temperature window. Ti_0.2-Ni_0.8-MOF showed the best denitration efficiency and reached 100% conversion in the temperature range of 200~400℃. Multiple characterizations were conducted to ascertain the properties of bimetallic Ti_x-Ni_1-x-MOFs materials (e.g., TGA, XRD, SEM, FT-IR, XPS and BET). Ti-doping in Ni-MOF can improve the atomic dispersion, and indicate a strong metal-metal interaction between Ti and Ni which was conducive to produce more efficient Ni-O-Ti sites and oxygen vacancies, strengthen the Ni²⁺+Ti⁴⁺ ↔ Ni³⁺+Ti³⁺ redox cycle, and thus improve the catalytic performance of NO reduction reaction by CO. Compared with solvothermal method, the preparation of Ti_0.2-Ni_0.8-MOF by microwave method exhibits the advantages of high synthesis efficiency, good crystallinity, fine and uniform grains, which further enhancing its low-temperature denitration effect.

Key words： CO-SCR metal-organic frameworks Ti_x-Ni_1-x-MOFs microwave method solvothermal method

收稿日期: 2022-04-25

PACS:

X511

基金资助:国家自然科学基金资助项目(21677022,22006007);工业生态与环境工程教育部重点实验室开放基金资助项目(KLIEEE-21-03)

通讯作者: 石勇,副教授,yongshi@dlut.edu.cn E-mail: yongshi@dlut.edu.cn

作者简介: 石勇(1975-),男,河南南阳人,副教授,博士,在大连理工大学从事环境催化材料合成、污染物监测及大气污染控制等方面的研究。发表论文70余篇。

引用本文:

石勇, 李橙, 黄磊, 熊巍, 肇启东, 孙健恒, 丁越. Ti_{_x}-Ni_{1-_x}-MOFs的制备及其CO选择性催化还原NO_{_x}研究[J]. 中国环境科学, 2022, 42(11): 5080-5087. SHI Yong, LI Cheng, HUANG Lei, XIONG Wei, ZHAO Qi-dong, SUN Jiang-heng, DING Yue. Preparation of Ti_x-Ni_1-x-MOFs and their selective catalytic reduction of NO_x by CO. CHINA ENVIRONMENTAL SCIENCECE, 2022, 42(11): 5080-5087.

链接本文:

http://www.zghjkx.com.cn/CN/ 或 http://www.zghjkx.com.cn/CN/Y2022/V42/I11/5080

[1]	蒋春来,宋晓晖,钟悦之,等.2010~2015年中国燃煤电厂NOx排放特征[J]. 中国环境科学, 2018,38(8):2903-2910. Jiang C L, Song X H, Zhong Y Z, et al. Characteristics of NOx emissions from coal-fired power plants in China from 2010 to 2015[J]. China Environmental Science, 2018,38(8):2903-2910.
[2]	李阳,陈敏鹏.长江经济带农业源非二氧化碳温室气体排放的时空特征[J]. 中国环境科学, 2020,40(5):2030-2039. Li Y, Chen M P. Spatial and temporal characteristics of non-carbon dioxide greenhouse gas emissions from agricultural sources in the Yangtze River Economic Belt[J]. China Environmental Science, 2020, 40(5):2030-2039.
[3]	陈小根,张茹杰,沈伯雄,等.以CO为还原剂的选择性催化还原NO催化剂研究进展[J]. 现代化工, 2020,40(5):5. Chen X G, Zhang R J, Shen B X, et al. Research progress in catalysts for selective catalytic reduction of NO with CO as reductant[J]. Modern Chemical Industry, 2020,40(5):5.
[4]	付玉秀,仲雪梅,常化振,等.铈钴复合氧化物催化剂催化CO-SCR反应机理研究[J]. 中国环境科学, 2018,38(8):2934-2940. Fu Y X, Zhong X M, Chang H Z, et al. Mechanism study on CO-SCR over Ce-Co-Ox mixed oxides catalysts[J]. China Environmental Science, 2018,38(8):2934-2940.
[5]	黄锦玉,孙波,孙义高,等.镍系低温SCR脱硝催化剂载体与助剂的研究进展[J]. 现代化工, 2021,41(1):34-37. Huang J Y, Sun B, Sun Y G, et al. Research progress in supports and additives of Ni-based catalysts for low temperature SCR De-NOx [J]. Modern Chemical Industry, 2021,41(1):34-37.
[6]	Sun X, Yong S, Wang Z, et al. A new type Ni-MOF catalyst with high stability for selective catalytic reduction of NOx with NH3[J]. Catalysis Communications, 2018,114:104-108.
[7]	戴波,张松,顾明言,等.Ce改性钒磷氧催化剂的制备及其脱硝性能研究[J]. 中国环境科学, 2019,39(1):126-133. Dai B, Zhang S, Gu M Y, et al. Preparation of supported VPO catalyst modified by Ce and the investigation of its denitration performance[J]. China Environmental Science, 2019,39(1):126-133.
[8]	Jiang H, Wang S, Wang C, et al. Selective catalytic reduction of NOx with NH3 on Cu-BTC-derived catalysts:influence of modulation and thermal treatment[J]. Catalysis Surveys from Asia, 2018,22(2):1-10.
[9]	Shi Y, Li C, Liu X, et al. MIL-100(Fe) as a new catalyst for selective catalysis reduction of NOx with ammonia[J]. Integrated Ferroelectrics, 2017,181(1):14-25.
[10]	石勇,牛丹阳,武卓敏,等.Ag/Cu3(BTC)2复合催化剂的制备及其NH3-SCR催化性能[J]. 中国环境科学, 2018,38(7):2445-2450. Shi Y, Niu D Y, Wu Z M, et al. Synthesis of Ag/Cu3(BTC)2 composite catalysts and their catalytic performance for NH3-SCR[J]. China Environmental Science, 2018,38(7):2445-2450.
[11]	刘晶,熊志波,周飞,等.新型铈钨钛复合氧化物催化还原脱硝机理[J]. 中国环境科学, 2018,38(5):1670-1676. Liu J, Xiong Z B, Zhou F, et al. The NH3-SCR mechanism of a novel cerium-tungsten-titanium mixed oxide catalyst prepared through the hydrothermal co-precipitation method modified by H2O2 complex[J]. China Environmental Science, 2018,38(5):1670-1676.
[12]	Li C, Shi Y, Yu F, et al. Preparation of metal-organic framework Cu+/Ni-MOF catalyst with enhanced catalytic activity for selective catalytic reduction of NOx[J]. Ferroelectrics, 2020,565(1):26-34.
[13]	Song K, Liang S, Zhong X, et al. Tailoring the crystal forms of the Ni-MOF catalysts for enhanced photocatalytic CO2-to-CO performance[J]. Applied Catalysis B:Environmental, 2022,309:121232.
[14]	Dey K, Sauerland S, Ouladdiaf B, et al. Magnetostructural coupling in ilmenite-type NiTiO3[J]. Physical Review. B, 2021,103(13):134438.
[15]	Wu X, Wang R, Du Y, et al. Performance enhancement of NH3-SCR via employing hydrotalcite-like precursor to induce the decoration of NiO by TiO2 phase[J]. Molecular Catalysis, 2019,467:150-160.
[16]	Liu B, J Liu, Xin L, et al. Unraveling reactivity descriptors and structure sensitivity in low-temperature NH3-SCR reaction over CeTiOx catalysts:A Combined Computational and Experimental Study[J]. ACS Catalysis, 2021,11(13):7613-7636.
[17]	Deng K. Optimized microwave-based synthesis of thermally stable inverse catalytic core-shell motifs for CO2 hydrogenation[J]. ACS Applied Materials & Interfaces, 2020,12(29):32591-32603.
[18]	Chen S, Xu X, Gao H, et al. Fine-tuning the metal oxo cluster composition and phase structure of Ni/Ti bimetallic MOFs for efficient CO2 reduction[J]. The Journal of Physical Chemistry C, 2021, 125(17):9200-9209.
[19]	Zhai M, Cheng Y, Jin Y, et al. Solvothermal synthesis of flower-like structure Cu-Mn bimetallic sulfide on Ni-foam for high-performance symmetric supercapacitors[J]. International Journal of Hydrogen Energy, 2019,44(26):13456-13465.
[20]	Nguyen H T, Tran K T, Van Tan L, et al. Microwave-assisted solvothermal synthesis of bimetallic metal-organic framework for efficient photodegradation of organic dyes[J]. Materials Chemistry and Physics, 2021,272:125040.
[21]	Chen C, Feng X, Zhu Q, et al. Microwave-assisted rapid synthesis of well-shaped MOF-74(Ni) for CO2 efficient capture[J]. Inorganic Chemistry, 2019,58(4):2717-2728.
[22]	Israr F, Kim D K, Kim Y, et al. Scope of various solvents and their effects on solvothermal synthesis of Ni-BTC[J]. Química Nova, 2016,39(6):669-675.
[23]	Ipadeola A K, Ozoemena K I. Alkaline water-splitting reactions over Pd/Co-MOF-derived carbon obtained via microwave-assisted synthesis[J]. RSC Adv., 2020,10(29):17359-17368.
[24]	Devarayapalli K C, Vattikuti S V P, Tvm S, et al. Facile synthesis of Ni-MOF using microwave irradiation method and application in the photocatalytic degradation[J]. Materials Research Express, 2019, 6(11):1150.
[25]	Xie S, Qin Q, Liu H, et al. MOF-74-M (M=Mn, Co, Ni, Zn, MnCo, MnNi, and MnZn) for low-temperature NH3-SCR and in situ DRIFTS study reaction mechanism[J]. ACS Applied Materials & Interfaces, 2020,12(43):48476-48485.
[26]	Wang D, Huang B, Shi Z, et al. Influence of cerium doping on Cu-Ni/activated carbon low-temperature CO-SCR denitration catalysts[J]. RSC Adv., 2021,11(30):18458-18467.
[27]	Xie S, Li L, Jin L, et al. Low temperature high activity of M (M=Ce, Fe, Co, Ni) doped M-Mn/TiO2catalysts for NH3-SCR and in situ DRIFTS for investigating the reaction mechanism[J]. Applied Surface Science, 2020,515:146014.
[28]	Gao S, Sui Y, Wei F, et al. Facile synthesis of cuboid Ni-MOF for high-performance supercapacitors[J]. Journal of Materials Science, 2018,53(3):6807-6818.
[29]	Liu Z, Sun G, Chen C, et al. Fe-doped Mn3O4 spinel nanoparticles with highly exposed Feoct-O-Mntet sites for efficient selective catalytic reduction (SCR) of NO with ammonia at low temperatures[J]. ACS Catalysis, 2020,10(12):6803-6809.
[30]	Shu S A, Guo J, Li J A, et al. The enhanced performance of Ti doped MnOx for the removal of NO with NH3[J]. Journal of the Taiwan Institute of Chemical Engineers, 2019,100:168-177.
[31]	He H, Zhang C, Wang Y, et al. Low-temperature selective catalytic reduction of NO with CO over Nix-MOF-5[J]. Journal of Materials Science, 2022,57(4):2502-2513.
[32]	Ramasubbu V, Kumar P R, Mothi E M, et al. Highly interconnected porous TiO2-Ni-MOF composite aerogel photoanodes for high power conversion efficiency in quasi-solid dye-sensitized solar cells[J]. Applied Surface Science, 2019,496(Dec.1):143646.1-143646.11.
[33]	Cao J, Rohani S, Liu W, et al. Influence of phosphorus on the NH3-SCR performance of CeO2-TiO2 catalyst for NO removal from co-incineration flue gas of domestic waste and municipal sludge[J]. Journal of Colloid and Interface Science, 2022,610:463-473.
[34]	Leukkunen P M, Rani E, Sasikala D A, et al. Synergistic effect of Ni-Ag-rutile TiO2 ternary nanocomposite for efficient visible-light-driven photocatalytic activity[J]. RSC Adv., 2020,10(60):36930-36940.
[35]	Chen L, Rui L, Li Z, et al. Effect of Ni doping in NixMn1-xTi10 (x=0.1-0.5) on activity and SO2 resistance for NH3-SCR of NO studied with in situ DRIFTS[J]. Catalysis Science & Technology, 2017,7(15):3243-3257.
[36]	Liu Z, Liu H, Feng X, et al. Ni-Ce-Ti as a superior catalyst for the selective catalytic reduction of NOx with NH3[J]. Molecular Catalysis, 2018,445:179-186.
[37]	Hu Z, Yong X, Li D, et al. Synergism between palladium and nickel on Pd-Ni/TiO2 for H2-SCR:A transient DRIFTS study[J]. Journal of Catalysis, 2020,381:204-214.
[38]	Liu Q, Tian Y, Ai H. Methanation of carbon monoxide on ordered mesoporous NiO-TiO2-Al2O3 composite oxides[J]. RSC Advances, 2016,6(25):2971-2978.
[39]	Y Zhang, Zhao L, Duan J, et al. Insights into deNOx processing over Ce-modified Cu-BTC catalysts for the CO-SCR reaction at low temperature by in situ DRIFTS[J]. Separation and Purification Technology, 2019,234:116081.
[40]	Wang Q, Xu H, Huang W, et al. Metal organic frameworks-assisted fabrication of CuO/Cu2O for enhanced selective catalytic reduction of NOx by NH3 at low temperatures[J]. Journal of Hazardous Materials, 2019,364:499-508.
[41]	Du Y, Liu J, Li X, et al. SCR performance enhancement of NiMnTi mixed oxides catalysts by regulating assembling methods of LDHs-Based precursor[J]. Applied Organometallic Chemistry, 2020,34(4):e5510.
[42]	Huang L, Shi Y, Xiong W, et al. Facile design of highly effective Fe-modified bimetallic Fex-Ni1−x-MOFs catalysts with rodlike structures for low-temperature NO reduction by CO[J]. Journal of Materials Science, 2021,56(16):9914-9928.
[43]	Ding Y, Shi Y, Xiong W, et al. Insights into N-coordinated bimetallic site synergy during NO selective catalytic reduction by CO[J]. ACS Applied Materials & Interfaces, 2021,13(48):57182-57192.