Treatment of emulsified oily wastewater by magnetic graphite oxide and magneto-induced enhanced effect

HU Zhuo-qi^1,2, CHEN Quan-yuan^1,2

Author information +

文章历史 +

摘要

以高铁酸钾为氧化剂，基于改进Hummers法制备了新型磁性氧化石墨材料，在SEM、FTIR、氮气吸脱附和表面接触角表征基础上，探究了该材料处理乳化含油废水的效果及磁致增强效应.结果表明：相较于石墨，磁性氧化石墨比表面积增大，表面有卷曲结构并负载着Fe₃O₄颗粒，具有含氧官能团，存在疏水性较强的微观孔隙结构.在外加磁场条件下，磁性氧化石墨团聚，形成疏水性宏观孔隙结构，利于乳化油滴的吸附和附着.磁性氧化石墨处理乳化含油废水的能力远好于石墨与粉末活性炭，且处理效率与磁场强度成正相关，COD去除率可达95%以上.使用后的磁性氧化石墨进行溶剂萃取或热处理，可以循环使用.磁性氧化石墨经过4次循环使用，热再生效率为92%，溶剂萃取再生效率为86%.以上研究为乳化含油废水的处理提供了一种有效的方法.

Abstract

Magnetic graphite oxide, a new type of material, was prepared by using potassium ferrate as an oxidant based on modified Hummers method. Based on SEM, FTIR, N₂ adsorption-desorption and surface contact angle measurements, the decontamination and magneto-induced enhanced effect of magnetic graphite oxide on the treatment of emulsified oily wastewater were investigated. The results showed that compared with graphite, specific surface areas of magnetic graphite oxide increased and the surface exhibited curly structure loaded with Fe₃O₄ particles, with oxygen-containing functional groups and strong hydrophobic micro-pore structures. In external magnetic field, magnetic graphite oxide agglomerated to form hydrophobic macroscopic pore structures, which were beneficial to adsorption and adhesion of emulsified oil droplets. As expected, magnetic graphite oxide was found to be much more effective to treat emulsified oily wastewater than graphite and powdered activated carbon. The efficiency of emulsified oily wastewater treatment was positive relevance to the magnetic field strength and removal of COD could exceed 95%. The used magnetic graphite oxide could be recycled by solvent extraction or heat treatment. The regeneration efficiencies were 92% and 86% for thermal treatment and solvent extraction for 4cycles. Therefore, the research above supports an effective method for the treatment of emulsified oily wastewater.

导出引用

胡卓祺, 陈泉源. 磁性氧化石墨处理乳化含油废水及磁致增强效应[J]. 中国环境科学. 2020, 40(7): 2970-2977

HU Zhuo-qi, CHEN Quan-yuan. Treatment of emulsified oily wastewater by magnetic graphite oxide and magneto-induced enhanced effect[J]. China Environmental Science. 2020, 40(7): 2970-2977

中图分类号： X703

参考文献

[1] Al-Anzi B S, Siang O C. Recent developments of carbon based nanomaterials and membranes for oily wastewater treatment[J]. Rsc Advances, 2017,7(34):20981-20994.
[2] 陈月芳,季振,林海,等.月桂酸改性生物质材料处理乳化油的机理[J]. 化工学报, 2014,65(6):2276-2284. Chen Y F, Ji Z, Lin H, et al. Removal mechanism of emulsified oil in wastewater by biologic materials modified with lauric acid[J]. CIESC Journal, 2014,65(6):2276-2284.
[3] 蒲维肖,刘丹丹,王志强,等.加热酸化-Fenton氧化处理乳化液废水[J]. 环境工程学报, 2013,7(10):4027-4031. Pu W X, Liu D D, Wang Z Q, et al. Treatment of emulsion wastewater with heating and acidification-Fenton oxidation[J]. Chinese Journal of Environmental Engineering, 2013,7(10):4027-4031.
[4] Yu L, Han M, He F. A review of treating oily wastewater[J]. Arab Journal of Physical Chemistry, 2017,10:S1913-S1922.
[5] Pintor A M A, Vilar V J P, Botelho C M S, et al. Oil and grease removal from wastewaters:Sorption treatment as an alternative to state-of-the-art technologies. A critical review[J]. Chemical Engineering Journal, 2016,297:229-255.
[6] 李继,吕小梅,张萍,等.柠檬酸盐强化UV/Fenton-生物法处理乳化油废水[J]. 中国环境科学, 2011,31(3):367-370. Li J, Lu X M, Zhang P, et al. Emulsion wastewater treatment by citrate enhanced UV/Fenton and combined with biological treatment[J]. China Environmental Science, 2011,31(3):367-370.
[7] Peng J X, Liu Q X, Xu Z H, et al. Novel magnetic demulsifier for water removal from diluted bitumen emulsion[J]. Energy & Fuels, 2012,26(5):2705-2710.
[8] Wang Q, Puerto M C, Warudkar S, et al. Recyclable amine-functionalized magnetic nano-particles for efficient demulsification of crude oil-in-water emulsions[J]. Environmental Science:Water Research & Technology, 2018,4(10):1553-1563.
[9] Ko S, Kim E S, Park S, et al. Amine functionalized magnetic nanoparticles for removal of oil droplets from produced water and accelerated magnetic separation[J]. Journal of Nanoparticle Research, 2017,19(4):132.
[10] Zhou S, Jiang W, Wang T H, et al. Highly hydrophobic, compressible, and magnetic poly-styrene/Fe₃O₄/graphene aerogel composite for oil-water separation[J]. Industrial & Engineering Chemistry Research, 2015,54(20):5460-5467.
[11] Liu S H, Xu Q F, Latthe S S, et al. Superhydrophobic/superoleophilic magnetic polyurethane sponge for oil/water separation[J]. Rsc Advances, 2015,5(84):68293-68298.
[12] Kim H J, Jeong H K. Direct reform of graphite oxide electrodes by using ambient plasma for supercapacitor applications[J]. Chemical Physics Letters, 2017,686:49-57.
[13] Wu Z B, Zhong H, Yuan X Z, et al. Adsorptive removal of methylene blue by rhamnolipid-functionalized graphene oxide from wastewater[J]. Water Research, 2014,67:330-344.
[14] Bannov A G, Manakhov A, Shibaev A A, et al. Synthesis dynamics of graphite oxide[J]. Thermochimica Acta, 2018,663:165-175.
[15] 周玉莲,于永波,黄湾,等.氧化石墨烯电催化高效降解有机染料RBk5[J]. 中国环境科学, 2019,39(11):4653-4659. Zhou Y L, Yu Y B, Huang W, et al. Electrocatalytic degradation of organic dye RBk5 by oxide grapheme[J]. Environmental Science, 2019,39(11):4653-4659.
[16] 张秀蓉,龚继来,曾光明,等.磁性氧化石墨烯制备及去除水中刚果红的研究[J]. 中国环境科学, 2013,33(8):1379-1385. Zhang X R, Gong J L, Zeng G M, et al. Synthesis of magnetic graphene oxide adsorbent for congo red removal from aqueous solution[J]. China Environmental Science, 2013,33(8):1379-1385.
[17] 刘伟,杨琦,李博,等.磁性石墨烯吸附水中Cr(Ⅵ)研究[J]. 环境科学, 2015,36(2):537-544. Liu W, Yang Q, Li B, et al. Adsorption of Cr(Ⅵ) on magnetic graphene from aqueous solution[J]. Environmental Science, 2015, 36(2):537-544.
[18] Yan H, Li H J, Tao X, et al. Rapid removal and separation of iron (II) and manganese (II) from micropolluted water using magnetic graphene oxide[J]. ACS Applied Materials & Interfaces, 2014,6(12):9871-9880.
[19] Yu H T, Zhang B W, Bulin C, et al. High-efficient synthesis of graphene oxide based on improved Hummers method[J]. Scientific Reports, 2016,6:36143.
[20] Peng L, Xu Z, Liu Z, et al. An iron-based green approach to 1-h production of single-layer graphene oxide[J]. Nature Communications, 2015,6:5716.
[21] Jin Z X, Wang X X, Sun Y B, et al. Adsorption of 4-n-nonylphenol and bisphenol-A on magnetic reduced graphene oxides:a combined experimental and theoretical studies[J]. Environmental Science & Technology, 2015,49(15):9168-9175.
[22] Kim F, Luo J, Cruz-Silva R, et al. Self-propagating domino-like reactions in oxidized graphite[J]. Advanced Functional Materials, 2010,20(17):2867-2873.
[23] Li Y, Yang N, Du T T, et al. Transformation of graphene oxide by chlorination and chloramination:Implications for environmental transport and fate[J]. Water Research, 2016,103:416-423.
[24] 曾红杰,余静,王盈盈.磁性吸附剂MZFS吸附偶氮染料中性红的性能及机理[J]. 中国环境科学, 2019,39(9):3814-3823. Zeng H J, Yu J, Wang Y Y. The performance and mechanism of adsorption azo dye neural red from aqueous solution using magnetic adsorbent MZFS[J]. China Environmental Science, 2019,39(9):3814-3823.
[25] 刘东京,张禛,吴江.载铜氮化碳纳米片对单质汞的吸附脱除特性[J]. 中国环境科学, 2019,39(5):1862-1868. Liu D J, Zhang Z, Wu J. Adsorption removal of elemental mercury on Cu-loaded carbon nitride nanosheet[J]. China Environmental Science, 2019,39(5):1862-1868.
[26] 丁元迪,周潼,王若云,等.金属基体上超疏水表面的制备及其机械耐久性的研究进展[J]. 表面技术, 2019,48(12):68-86. Ding Y D, Zhou T, Wang R Y, et al. Research progress of the preparation and mechanical durability of superhydrophobic surfaces on metal substrates[J]. Surface Technology, 2019,48(12):68-86.
[27] 佟瑞利,赵娜娜,王湘英,等. Fe₃O₄纳米颗粒的制备及其净化含油污水的研究[J]. 化学工程, 2009,37(7):47-50. Tong R L, Zhao N N, Wang X Y, et al. Preparation of Fe₃O₄ nanoparticles and their purification of oil-bearing wastewater[J]. Chemical Engineering (China), 2009,37(7):47-50.
[28] 杨敬一,严良,徐心茹. Fe₃O₄纳米颗粒在含油污水处理中的应用[J]. 工业水处理, 2016,36(7):82-85. Yang J Y, Yan L. Xu X R. Application of Fe₃O₄ nano-particles to the treatment of oil-bearing wastewater. Industrial Water Treatment, 2016,36(7):82-85.
[29] Nabeel Rashin M, Kutty R G, Hemalatha J. Novel coconut oil based magnetite nanofluid as an ecofriendly oil spill remover[J]. Industrial & Engineering Chemistry Research, 2014,53(40):15725-15730.
[30] Lü T, Chen Y, Qi D M, et al. Treatment of emulsified oil wastewaters by using chitosan grafted magnetic nanoparticles[J]. Journal of Alloys and Compounds, 2017,696:1205-1212.
[31] Zhang J R, Li Y M, Bao M T, et al. Facile fabrication of cyclodextrin-modified magnetic particles for effective demulsification from various types of emulsions[J]. Environmental Science & Technology, 2016,50(16):8809-8816.
[32] Gulistan A S. Oil removal from produced water using natural materials[D]. American University of Sharjah, 2014.
[33] Diraki A, Mackey H, McKay G, et al. Removal of oil from oil-water emulsions using thermally reduced graphene and graphene nanoplatelets[J]. Chemical Engineering Research and Design, 2018, 137:47-59.
[34] Sabio E, González E, González J F, et al. Thermal regeneration of activated carbon saturated with p-nitrophenol[J]. Carbon, 2004, 42(11):2285-2293.
[35] Dutta T, Kim T, Vellingiri K, et al. Recycling and regeneration of carbonaceous and porous materials through thermal or solvent treatment[J]. Chemical Engineering Journal, 2019,364:514-529.