Catalytic performance of Pt-supported modified red mud catalyst for toluene catalytic oxidation
FANG Hong-ping1,2, LIANG Wen-jun2, MA Chen2, MA Lian-gang1, LI Gui-xian1
1. Faculty of Resource and Environmental Engineering, Guizhou Institute of Technology, Guiyang 550003, China; 2. Key Laboratory of Beijing on Regional Air Pollution Control, Faculty of Environment and Life, Beijing University of Technology, Beijing 100124, China
Abstract:A low-cost modified red mud supported Pt catalyst was prepared by impregnation method, and the effect of Pt content on catalytic oxidation activity of toluene on Pt/MRM catalyst was investigated. 0.4Pt/MRM showed the best catalytic activity, and the toluene conversion rate reached 100% at 230℃. The catalytic activity of 0.4Pt/MRM was still higher when the airspeed was up to 120000h-1. Toluene can be oxidized effectively in a wide range of toluene concentrations. XRD, FT-IR, BET, H2-TPR and O2-TPD were used to characterize. The specific surface area of MRM was significantly higher than RM, which can disperse the active component Pt better and become a suitable catalyst carrier for the active component Pt. The prepared xPt/MRM catalyst had high surface area and good pore structure. The interaction between Fe2O3 and Pt species in the modified red mud increased the total oxygen desorption capacity of the catalyst, improved the mobility of oxygen on the catalyst surface, and the catalytic efficiency.
[1] He Y, Shen J, Alharbi N S, et al. Volatile organic compounds degradation by nonthermal plasma:a review[J]. Environmental Science and Pollution Research, 2023,30(12):32123-32152. [2] 游志敏,蒋思成,程燊昱,等.微波辐射下La-Mn-Co金属氧化物的甲苯降解性能[J]. 湘潭大学学报(自然科学版), 2023,45(6):85-99. You Z M, Jiang S C, Cheng S Y, et al. Catalytic performance of La-Mn-Co oxides for toluene oxidation under microwave irradiation[J]. Journal of Xiangtan University (Natural Science Edition), 2023, 45(6):85-99. [3] Wang X X, Wei T, Wen Y C, et al. Catalytic ozonation of toluene and dichloromethane mixture at low temperatures over modified MnOx- based catalyst[J]. Process Safety and Environmental Protection, 2023, 171:447-458. [4] Li X Q, Zhang L, Yang Z Q, et al. Adsorption materials for volatile organic compounds (VOCs) and the key factors for VOCs adsorption process:A review[J]. Separation and Purification Technology, 2020, 235. DOI 10.1016/j.seppur.2019.116213 [5] 肖惠平,马增益,贾海龙,等.以氧化铝中空小球为床料的流化床焚烧甲苯气体试验研究[J]. 能源工程, 2013,(1):60-63. Xiao H P, Ma Z Y, Jia H L, et al. Experimental research on methylbenzene air fluidized bed incineration with small hollow Al2O3 bed material[J]. Energy Engineering, 2013,(1):60-63. [6] Zhao S Z, Wen Y F, Liu X J, et al. Formation of active oxygen species on single-atom Pt catalyst and promoted catalytic oxidation of toluene[J]. Nano Research, 2020,13(6):1544-1551. [7] Castillo A, Biard P F, Guiheneuf S, et al. Assessment of VOC absorption in hydrophobic ionic liquids:Measurement of partition and diffusion coefficients and simulation of a packed column[J]. Chemical Engineering Journal, 2019,360:1416-1426. [8] Chen L, Li K L, Yang Y, et al. Amorphous SnO2 decorated ZnSn(OH)6 promotes interfacial hydroxyl polarization for deep photocatalytic toluene mineralization[J]. Journal of Hazardous Materials, 2023,444. DOI 10.1016/j.jhazmat.2022.130436 [9] Yan Y X, Wang M L, Jin B Q, et al. Performance evaluation and microbial community analysis of the biofilter for removing grease and volatile organic compounds in the kitchen exhaust fume[J]. Bioresource Technology, 2021,319. DOI 10.1016/j.biortech.2020. 124132 [10] Kone N A, Belkessa N, Serhane Y, et al. Chlorobenzene mineralization using plasma/photocatalysis hybrid reactor:Exploiting the Synergistic Effect[J]. Catalysts, 2023,13(2). DOI 10.3390/catal13020431 [11] He Y, Shen J, Alharbi N S, et al. Volatile organic compounds degradation by nonthermal plasma:a review[J]. Environmental Science and Pollution Research, 2023,30(12):32123-32152. [12] Zhang X L, Wen M C, Liao K W, et al. Preferential removal of aromatics-dominated electronic industrial emissions using the integration of spray tower and photocatalysis technologies[J]. Journal of Cleaner Production, 2022,364. DOI 10.1016/j.jclepro.2022.132706 [13] Gaalova J, Topka P. Gold and ceria as catalysts for VOC abatement:A review[J]. Catalysts, 2021,11(7):789. [14] Guo Y L, Wen M C, Li G Y, et al. Recent advances in VOC elimination by catalytic oxidation technology onto various nanoparticles catalysts:a critical review[J]. Applied Catalysis B- Environmental, 2021,281. DOI 10.1016/j.apcatb.2020.119447 [15] Patangia J, Saravanan T J, Kabeer K, et al. Study on the utilization of red mud (bauxite waste) as a supplementary cementitious material:Pathway to attaining sustainable development goals[J]. Construction and Building Materials, 2023,375. DOI 10.1016/j.conbuildmat.2023. 131005 [16] Mishra B, Gostu S. Materials sustainability for environment:Red-mud treatment[J]. Frontiers of Chemical Science and Engineering, 2017, 11(3):483-496. [17] 赵梓,赵爱春,叶鑫,等.赤泥在铁、钪元素回收及建筑材料领域的研究进展[J]. 中国有色冶金, 2023,52(2):96-103. Zhao Z, Zhao A C, Ye X, et al. Research progress of red mud in iron and scandium recovery and building materials[J]. China Nonferrous Metallurgy, 2023,52(2):96-103. [18] Joseph C G, Taufiq-Yap Y H, Krishnan V, et al. Application of modified red mud in environmentally-benign applications:A review paper[J]. Environmental Engineering Research, 2020,25(6):795-806. [19] Wang L, Sun N, Tang H H, et al. A review on comprehensive utilization of red mud and prospect analysis[J]. Minerals, 2019, 9(6):362. [20] Ng P F, Li L, Wang S B, et al. Catalytic ammonia decomposition over industrial-waste-supported Ru catalysts[J]. Environmental Science & Technology, 2007,41(10):3758-3762. [21] Wang B, Ma J, Wang D, et al. Acid-pretreated red mud for selective catalytic reduction of NOx with NH3:Insights into inhibition mechanism of binders[J]. Catalysis Today, 2021,376:247-254. [22] Ebrahiminejad M, Karimzadeh R. Hydrocracking and hydrodesulfurization of diesel over zeolite beta-containing NiMo supported on activated red mud[J]. Advanced Powder Technology, 2019,30(8):1450-1461. [23] Liu Q R, Li H P, Fang X K, et al. Preparation of modified red mud-supported Fe catalysts for hydrogen production by catalytic methane decomposition[J]. Journal of Nanomaterials, 2017,2017. DOI 10.1155/2017/8623463 [24] Ordonez S, Sastre H, Diez F V. Characterisation and deactivation studies of sulfided red mud used as catalyst for the hydrodechlorination of tetrachloroethylene[J]. Applied Catalysis B-Environmental, 2001, 29(4):263-273. [25] Zhang C, Li S H, Wu C L, et al. Preparation and Characterization of Pt@Au/Al2O3 Core-Shell Nanoparticles for Toluene Oxidation Reaction[J]. Acta Physico-Chimica Sinica. 2020,36(8). DOI 10.3866/PKU.WHXB201907057 [26] Abbasi Z, Haghighi M, Fatehifar E, et al. Synthesis and physicochemical characterizations of nanostructured Pt/Al2O3-CeO2 catalysts for total oxidation of VOCs[J]. Journal of Hazardous Materials, 2011,186(2/3):1445-1454. [27] 任思达,梁文俊,王昭艺,等.Ce掺杂对Pd/γ-Al2O3催化燃烧甲苯性能的影响[J]. 中国环境科学, 2019,39(7):2774-2780. Ren S D, Liang W J, Wang Z Y, et al. Effect of Ce doping on the performance of Pd/γ-Al2O3 catalytic combustion of toluene[J]. China Environmental Science, 2019,39(7):2774-2780. [28] Cao J L, Yan Z L, Deng Q F, et al. Homogeneous precipitation method preparation of modified red mud supported Ni mesoporous catalysts for ammonia decomposition[J]. Catalysis Science & Technology, 2014,4(2):361-368. [29] Hu Z P, Zhu Y P, Gao Z M, et al. CuO catalysts supported on activated red mud for efficient catalytic carbon monoxide oxidation[J]. Chemical Engineering Journal, 2016,302:23-32. [30] Alp A, Goral M S. The influence of soda additive on the thermal properties of red mud[J]. Journal of Thermal Analysis and Calorimetry, 2003,73(1):201-207. [31] An N, Yu Q, Liu G, et al. Complete oxidation of formaldehyde at ambient temperature over supported Pt/Fe2O3 catalysts prepared by colloid-deposition method[J]. Journal of Hazardous Materials, 2011, 186(2):1392-1397. [32] Perez J, Lucio-Ortiz C J, de la Rosa J R, et al. Dry Reforming of Methane for Hydrogen Production Using Bimetallic Catalysts of Pt-Fe Supported on gamma-Alumina[J]. Chemistryselect, 2021,6(45):12685-12695. [33] Peng R S, Li S J, Sun X B, et al. Size effect of Pt nanoparticles on the catalytic oxidation of toluene over Pt/CeO2 catalysts[J]. Applied Catalysis B-Environmental, 2018,220:462-470. [34] Rombi E, Ferino I, Monaci R, et al. Toluene ammoxidation on alpha- Fe2O3-based catalysts[J]. Applied Catalysis a-General, 2004,266(1):73-79. [35] 崔维怡,王圣公,王琳琳,等.负载型Pt-Fe/Al2O3催化剂用于室温催化氧化甲醛[J]. 化工进展. 2019,38(3):1427-1433. Cui W Y, Wang S G, Wang L L, et al. Pt-Fe/Al2O3 catalysts for removal of formaldehyde at ambient temperature[J]. Chemical Industry and Engineering Progress, 2019,38(3):1427-1433. [36] An N H, Wu P, Li S Y, et al. Catalytic oxidation of formaldehyde over PtiFe2O3 catalysts prepared by different method[J]. Applied Surface Science, 2013,285:805-809. [37] Zhao S, Hu F Y, Li J H. Hierarchical core-shell Al2O3@Pd-CoAlO microspheres for low-temperature toluene combustion[J]. Acs Catalysis, 2016,6(6):3433-3441. [38] Chen X, Chen X, Cai S C, et al. Catalytic combustion of toluene over mesoporous Cr2O3-supported platinum catalysts prepared by in situ pyrolysis of MOFs[J]. Chemical Engineering Journal, 2018,334:768-779. [39] Li J, Na H B, Zeng X L, et al. In situ DRIFTS investigation for the oxidation of toluene by ozone over Mn/HZSM-5, Ag/HZSM-5 and Mn-Ag/HZSM-5catalysts[J]. Applied Surface Science, 2014,311:690-696. [40] Rainone F, Bulushev D A, Kiwi-Minsker L, et al. DRIFTS and transient-response study of vanadia/titania catalysts during toluene partial oxidation[J]. Physical Chemistry Chemical Physics, 2003, 5(20):4445-4449. [41] Guo M M, Li K, Liu L Z, et al. Manganese-based multi-oxide derived from spent ternary lithium-ions batteries as high-efficient catalyst for VOCs oxidation[J]. Journal of Hazardous Materials, 2019,380. DOI 10.1016/j.jhazmat.2019.120905 [42] Yang W H, Su Z A, Xu Z H, et al. Comparative study of alpha-, beta-, gamma- and delta-MnO2 on toluene oxidation:Oxygen vacancies and reaction intermediates[J]. Applied Catalysis B-Environmental, 2020, 260. DOI 10.1016/j.apcatb.2019.118150